Abstract: This is an article in the field of metallurgical engineering. In this article, TiH₂ powder was selected as the experimental raw material to study the sintering behavior of TiH₂ powder under different pressing pressure and holding time in cold isostatic pressing, to reveal the effects of pressing pressure and holding time on the shrinkage as well as the relative density of TiH₂ sintered specimens, in order to improve the density of the billet and the performance of the products. The results show that the shrinkage of the sintered sample decreases with the increase of the pressing pressure, and when the pressing pressure reaches 400 MPa, the pressing pressure has little effect on the relative density of the sintered sample. For the consideration of the sample preparation efficiency and the pressing pressure limit of the cold isostatic press, the pressing pressure should not exceed 400 Mpa. The shrinkage of sintered samples decreases with the increase of holding time, and when the holding time reaches 20 min, the relative density of sintered samples changes little with the extension of holding time. For the consideration of sample preparation efficiency, the suitable holding time is 15～20 min.